Structural and magnetic properties of single crystal (311) plane of Co0.3Zn0.7Fe2O4 ferrite by ceramic method.

Jun 9, 2016, 11:15 AM
Room Th

Room Th

Oral presentaion Material Physics, Nanoscale Physics and Nanotechnology Session XXII


Mr Anuwat Hassadee (bansomdejchaopraya rajabhat University, Bangkok, 10600)


Anuwat Hassadee1*, Kedsarin Meemon1, and Tippavan Hongkachern1
1Department of Science, Faculty of Education, Bansomdejchaopraya Rajabhat University, Bangkok, 10600

*E-mail: anuwat8652@hotmail.com

Co0.3Zn0.7Fe2O4 ferrites were prepared by ceramic process and sintered 1250oC, 1300oC and 1350oC. The crystal structural, morphological and magnetic properties of ferrite were determined by X-ray diffractometry (XRD), scanning electron microscopy (SEM), and vibrating sample magnetometer (VSM) respectively. The result of samples show that cubic spinel ferrite and the crystallite size increases from 6.80 Å to 9.08 Å with the increase sintering temperature from 1250oC to 1350oC. The magnetization and cocercivity of samples were found to be ~22 emu/g and 29 Oe, respectively which independent of sintering temperature. The single crystal Co0.3Zn0.7Fe2O4 ferrite can be prepared at temperature 1350oC (rate 3oC/min) for 2 h. It was found that single crystal (311) plane.

Keywords : Co0.3Zn0.7Fe2O4: single crystal: ceramic method