Synthesis and characterization from Zn1-xCoxFe2O4 nanostructures prepared by hydrothermal method

20 May 2015, 14:00
3h 30m
Board: MAG-01
Poster presentation Magnetic and Semiconductor Physics Poster-1

Speaker

Mr narinthorn Wiriya (Department of Material Science and Nanotechnology, Faculty of Science, Khon Kaen University, Khon Kaen 40002, Thailand)

Description

In this work, we report the synthesis of Zn${}_x$Co${}_{1-x}$Fe${}_2$O${}_4$ nanoparticles ($x$ = 0.0, 0.2, 0.4, 0.6, 0.8, and 1.0) prepared by hydrothermal method. The results of XRD, SEM and TEM showed that were cubic spinel structure with the particle size in the range of 7-17 nm. The IR spectra of Zn${}_{1-x}$Co${}_x$Fe${}_2$O${}_4$ nanoparticles exposed the intrinsic stretching vibrational modes of the metals at the tetrahedral and octahedral sites. The magnetic properties as measured by VSM indicated that all sample behaved ferromagnetic with saturation magnetization (Ms) and coercivity of 15-52 emu/g and 72-257 Oe, respectively. The XANES spectra were used to identify the oxidation state of Zn, Co and Fe ions using K-edge profiles by shifts of separate edge. The oxidation state of Zn and Co cations are found to be +2 and +2,+3 respectively. The Fe${}^{2+}$ and Fe${}^{3+}$ cations are preferable to be at preference for the tetrahedaral and octahedral sites, respectively.

Primary author

Mr narinthorn Wiriya (Department of Material Science and Nanotechnology, Faculty of Science, Khon Kaen University, Khon Kaen 40002, Thailand)

Co-author

Mr Ekaphan Swatsitang (Department of Physics, Faculty of Science, Khon Kaen University, Khon Kaen 40002, Thailand)

Presentation Materials

There are no materials yet.
Your browser is out of date!

If you are using Internet Explorer, please use Firefox, Chrome or Edge instead.

Otherwise, please update your browser to the latest version to use Indico without problems.

×