Dielectric Properties of 0-3 Barium Zirconate Titanate˗Portland Cement Composites at 40% BZT Content with Carbon Addition

21 May 2015, 13:00
3h 30m
Board: MNA-63
Poster presentation Material Physics, Nanoscale Physics and Nanotechnology

Speaker

Dr Ruamporn Potong (Division of Physics, Faculty of Science and Technology, Rajamangala University of Technology Thanyaburi, Pathum Thani, THAILAND 12110)

Description

The 0-3 barium zirconate titanate˗portland cement composites with carbon addition which are expected to find application in civil engineering. The barium zirconate titanate, portland cement and carbon powder were fabricated using 425 µm barium zirconate titanate particle size at 40% by volume and varying carbon addition at 0.3-2% by volume. The composites were then cured at 60 ºC for 3 days before measurements. The dielectric constant and the dielectric loss at room temperature and various frequencies of the barium zirconate titanate˗portland cement composites with different carbon contents were investigated. The results show that the dielectric constant of composites was found to increase as carbon content increases, and that the dielectric constant was increase to the value of $\approx$310 for a carbon content of 2%.

Primary author

Dr Ruamporn Potong (Division of Physics, Faculty of Science and Technology, Rajamangala University of Technology Thanyaburi, Pathum Thani, THAILAND 12110)

Co-authors

Dr Arnon Chaipanich (Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai, THAILAND 50200) Dr Rianyoi Rattiyakorn (Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai, THAILAND 50200)

Presentation Materials

There are no materials yet.