Login

CEC-ICMC 2015 - Timetable, Abstracts and Presentations

28 June 2015 to 2 July 2015
JW Marriott Starr Pass Resort
Etc/GMT-7 timezone

Support

Session

M3PoA - Superconductor Materials IV: Properties and Applications

M3PoA
1 Jul 2015, 09:00
JW Marriott Starr Pass Resort

JW Marriott Starr Pass Resort

Tucson, Arizona USA

Conveners

M3PoA - Superconductor Materials IV: Properties and Applications

  • Pei Li (Fermi National Accelerator Laboratory)
  • Matthias Mentink (CERN)

Presentation materials

There are no materials yet.

  1. 501. Assessment of Critical Factors Affecting the Performance of Trapped Field Magnets using Thin Film Superconductor Tapes
    Ms Kavita Selva (Clear Lake High School)
    01/07/2015, 09:00
    ICMC-02 - RE123 Conductors Processing and Properties
    Poster Presentation
    Thin film superconductor tapes are composites with 98% metallic content and so, Trapped Field Magnets (TFMs) using such tapes can be much more robust than those using bulk superconductors. Trapped magnetic field profiles were investigated in Zr-added (Gd,Y)Ba2Cu3Ox tapes stacked in a criss cross configuration with three 12 mm wide tapes per layer. A crisscross arrangement of the tapes was...
  2. 412. Effect of heat treatment and test barrel materials on critical current measurements of Ag/Bi2212 round wires using ITER barrel configurations
    Tengming Shen (Fermilab)
    01/07/2015, 09:00
    ICMC-03 - BSCCO Processing and Properties
    Poster Presentation
    Critical current measurement for Ag/Bi-2212 wires has been typically performed by mounting a short sample (4-10 cm long) heat treated standalone at ~830 °C on a room temperature G-10 sample holder and cooling them down to cryogenic temperatures. During this process samples experience a huge temperature and strain change. This strain effect has not been carefully considered for critical...
  3. 510. Effect of Transport Current on Magnetization of an IBAD Coated Conductor
    Cory Myers (Ohio State University)
    01/07/2015, 09:00
    ICMC-02 - RE123 Conductors Processing and Properties
    Poster Presentation
    In this work susceptometry was used to measure the magnetization, as a function of transverse applied magnetic field, sample temperature, and transport current of an IBAD coated conductor. The M-H loops of four samples of the conductor which had different lengths (from 12-4 mm), and which were approximately 3 cm in length and approximately 100 µm in thickness, were measured. The widths were...
  4. 458. High Strain and Twisting Tolerance in AIMI and PIT MgB2 Strands
    Yuan Yang (OSU)
    01/07/2015, 09:00
    ICMC-04 - MgB2 Processing and Properties
    Poster Presentation
    The influence of strand bending and twisting on the critical current density, Jc, and n-value of MgB2 multifilamentary strands were evaluated, and the field and temperature dependence of the transport properties was evaluated for MgB2 strands. Two types of MgB2 strands were fabricated; (i) advanced internal magnesium infiltration method (AIMI) strands, and (ii) powder in tube method (PIT) type...